The rupture-test characteristics at 1350 degrees F of two wrought alloys in the solution-treated and aged condition, NR-82 (6059 modified-low carbon) and NR-84 (N-155 modified-low carbon), and three precision-cast alloys in aged condition, NR-71 (X-40), NR-87 (Co-Cr-Ni base-9Mo) and NR-90 (Co-Cr-Ni base-5Mo, 5W) are reported. The properties are shown to compare favorably with those of the strongeest similar alloys previously investigated. A correlation of NACA and OSRD data is presented, showing the variation of ruture strengths with temperature for the alloys between 1350 degrees and 2000 degrees F.